HDPE KT10000UE

Description

Dow HDPE KT 10000 UE is a UV-stabilised resin with a very narrow molecular weight distribution. It was developed to impart excellent stiffness, combined with good impact strength to injection molded parts at minimum warpage.

Specification

General

Material Status

Commercial: Active

Availability

Asia Pacific
Europe

Additive

Antiblock: No

Processing Aid: No

Slip: No

Forms

Pellets

Physical	Nominal Value	Unit	Test Method
Density / Specific Gravity	0.966		ASTM D792
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	8.0	g/10 min
190°C/5.0 kg	22	g/10 min
Spiral Flow	28.9	in	Internal Method
Molding Shrinkage - Flow	0.021	in/in	ASTM D955
Environmental Stress-Cracking Resistance (ESCR) (100% Antarox CO-630, Compression Molded)	2.50	hr	ASTM D1693
Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, Compression Molded)	66		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield, Compression Molded	4210	psi
Break, Compression Molded	4640	psi
Tensile Elongation (Break, Compression Molded)	800	%	ASTM D638
Flexural Modulus - 2% Secant (Compression Molded)	152000	psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength (Compression Molded)	36.6	ft·lb/in²	ASTM D1822