LLDPE 2607G

Description

Dowlex LLDPE 2607G is a linear low-density polyethylene for cast film, blown film, and coextrusion equipment that offers excellent processability. Known for its excellent balance of processability, mechanical performance, and stretchability properties, it is a suitable, cost-effective solution for a range of applications.

Specification

General

Material Status

Commercial: Active

Availability

Europe

Additive

Antiblock: No

Processing Aid: No

Slip: No

Agency Ratings

EU No 10/2011

FDA FCN 741

Forms

Pellets

Physical	Nominal Value	Unit	Test Method
Density / Specific Gravity	0.920		ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.3	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	0.91	mil
Film Puncture Energy (0.91 mil)	1420	in·lb
Film Puncture Force (0.91 mil)	9.89	lbf
Tensile Strength			ASTM D882
MD : Yield, 0.91 mil	1160	psi
TD : Yield, 0.91 mil	1160	psi
MD : Break, 0.91 mil	5080	psi
TD : Break, 0.91 mil	4210	psi
Tensile Elongation			ASTM D882
MD : Break, 0.91 mil	460	%
TD : Break, 0.91 mil	700	%
Dart Drop Impact (0.91 mil)	150	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 0.91 mil	190	g
TD : 0.91 mil	420	g
Film Stretch Performace - Max Elongation (0.9 mil)	350	%	Internal Method
Film Stretch Performace - Max Stretch Force (0.9 mil)	37000	g	Internal Method

Additional Information
Film Properties: Cast Film fabrication at 250 m/min.

Extrusion Notes
Fabrication Conditions For Cast Film Extrusion: Chill Roll Temperature: 20 - 40°C Melt Temperature: 220 - 280°C Recommended Gauge Range: 10 - 35 µm

Related beads

LLDPE 1002XBU

SPDC FC21HS

Dow 7047NT7

LLDPE 500026

LLDPE 218BJ

Sabic 219ZJ

XUS 89770.00 Experimental Polyethylene Resin

Marlex D139FK

ExxonMobil 2018HA

Sabic 318CNJ

ExxonMobil 1002AY

SPDC FC21HN