Lotrène® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
General
Material Status
Availability
Additive
Features
Uses
Agency Ratings
Processing Method
Physical
Density / Specific Gravity
ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
ASTM D1238
Films
Secant Modulus
ASTM D882
1% Secant, MD
: 1.6 mil, Blown Film
ASTM D882
1% Secant, TD
: 1.6 mil, Blown Film
ASTM D882
Tensile Strength
ASTM D882
MD
: Yield, 1.6 mil, Blown Film
ASTM D882
TD
: Yield, 1.6 mil, Blown Film
ASTM D882
MD
: Break, 1.6 mil, Blown Film
ASTM D882
TD
: Break, 1.6 mil, Blown Film
ASTM D882
Tensile Elongation
ASTM D882
MD
: Break, 1.6 mil, Blown Film
ASTM D882
TD
: Break, 1.6 mil, Blown Film
ASTM D882
Dart Drop Impact (1.6 mil, Blown Film)
ASTM D1709
Elmendorf Tear Strength
ASTM D1922
MD
: 1.6 mil, Blown Film
ASTM D1922
TD
: 1.6 mil, Blown Film
ASTM D1922
Thermal
Vicat Softening Temperature
ASTM D1525
Peak Crystallization Temperature (DSC)
Internal Method
Optical
Gloss (45°, 1.57 mil, Blown Film)
ASTM D2457
Haze (1.57 mil, Blown Film)
ASTM D1003