Dow LLDPE 2645.11G Data Sheet - Globexvn.com
Dow LLDPE 2645.11G Data Sheet - Globexvn.com
  • Dow LLDPE 2645.11G Data Sheet - Globexvn.com
  • Dow LLDPE 2645.11G Data Sheet - Globexvn.com

Dow LLDPE 2645.11G

Thương hiệuDow

Chỉ số chảy

0.9

Mã nhựa

LLDPE

Liên hệ tư vấn

Loại: LLDPE 2645.11G
Xuất xứ: Hoa Kỳ
Thương hiệu: Dow
Ứng dụng: Màng phủ nông nghiệp, túi nhựa, bao bì.

Mô tả

Nhựa Dow LLDPE 2645.11G xuất xứ Hoa Kỳ có chỉ số chảy (MI) = 0.9. Ứng dụng: Màng phủ nông nghiệp, túi nhựa, bao bì.

Datasheet

General
Material Status
Commercial: Active
Availability
Asia Pacific
Latin America
Additive
Antiblock: 3000 ppm
Processing Aid: No
Slip: 1200 ppm
Agency Ratings
EU No 10/2011
FDA FCN 1539
Forms
Pellets
Processing Method
Blown Film
Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity
0.923
 
 ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
0.90
g/10 min
 ASTM D1238
Films
Nominal Value
Unit
Test Method
Film Thickness - Tested
2.0
mil
Film Puncture Resistance (2.0 mil)
80.0
ft·lb/in³
 Internal Method
Secant Modulus ASTM D882
2% Secant, MD : 2.0 mil
24400
psi
 ASTM D882
2% Secant, TD : 2.0 mil
34500
psi
 ASTM D882
Tensile Strength ASTM D882
MD : Yield, 2.0 mil
2060
psi
 ASTM D882
TD : Yield, 2.0 mil
2120
psi
 ASTM D882
MD : Break, 2.0 mil
7080
psi
 ASTM D882
TD : Break, 2.0 mil
5680
psi
 ASTM D882
Tensile Elongation ASTM D882
MD : Break, 2.0 mil
660
%
 ASTM D882
TD : Break, 2.0 mil
740
%
 ASTM D882
Dart Drop Impact (2.0 mil)
300
g
 ASTM D1709A
Elmendorf Tear Strength ASTM D1922
MD : 2.0 mil
720
g
 ASTM D1922
TD : 2.0 mil
1000
g
 ASTM D1922
Thermal
Nominal Value
Unit
Test Method
Vicat Softening Temperature
225
°F
 ASTM D1525
Melting Temperature (DSC)
248
°F
 Internal Method
Optical
Nominal Value
Unit
Test Method
Gloss (45°, 2.00 mil)
56
 
 ASTM D2457
Haze (2.00 mil)
14.0
%
 ASTM D1003
Extrusion Notes
Fabrication Conditions For Blown Film:
  • Screw Size: 2.5 in. (63.5 mm) 30:1L/D
  • Screw Type: DSBII
  • Die Gap: 70 mil (1.8 mm)
  • Output: 10 lb/hr/in. of die circumference
  • Die Diameter: 6 in.
  • Blow-Up Ratio: 2.5 : 1